Gd-123 superconducting phase was prepared by solid-state reaction technique. Single-walled carbon nanotubes (SWCNTs) were added in Gd-123 superconducting matrix with different concentrations during the final sintering process to obtain (SWCNTs) x x GdBa2Cu3O 7−δ 7−δ (x = 0.0–0.1 wt.%) nanoparticles–superconductor composite. The influence of SWCNTs addition on the phase formation, structural, morphological, superconducting and dielectric properties of Gd-123 phase was investigated. It was found that SWCNTs addition enhance the phase formation and does not change the crystal structure of the host Gd-123 superconducting phase. The superconducting properties of Gd-123 samples were improved after the addition of SWCNTs up to x = 0.06 wt.% due to the enhancement in intergrain connectivity by healing up of micro-cracks and reduction of defects, while these properties were retarded with further increase in x. The dielectric response of (SWCNTs) x x Gd-123 superconducting phase with x = 0.0, 0.01, 0.04, 0.05, 0.06 and 0.1 wt.% was measured from 100 KHz to 5 MHz at 77 K. The results reveal that for both real (ε ′ 𝜀′ ) and imaginary (ε ′′ 𝜀″ ) parts of dielectric constant, the frequency of dispersion increased by increasing SWCNTs amount up to 0.06 wt.%, then this frequency shifted to lower values for x > > 0.06 wt.%. The results were discussed according to the presence and interference of both interfacial and dipolar polarizations.